Name: Thermosetting Acrylic Film Adhesive TAF-130
Brand: Coatingsink
SKU: thermosetting-acrylic-film-adhesive
Availability: PreOrder

Question 1

What cure cycle is recommended for TAF-130 on aluminium substrates?

Accepted Answer

The standard cycle is 130°C for 30 minutes under 0.3–0.5 MPa contact pressure. For aluminium sections thicker than 3 mm, extend dwell time to 45 minutes to ensure complete cross-linking through the bondline.

Question 2

Is an FST-compliant grade of TAF-130 available for aerospace cabin interiors?

Accepted Answer

Yes. The FST variant meets FAR 25.853 flame, smoke, and toxicity requirements. Mechanical properties and cure schedule are identical to the standard grade; specify the FST suffix when ordering.

Question 3

How does TAF-130 perform under cyclic fatigue loading compared to liquid epoxy film adhesives?

Accepted Answer

The cross-linked acrylic network dissipates cyclic strain more effectively than single-part epoxies. TAF-130 retains >80% of initial lap shear strength after 10⁶ cycles at ±5 MPa (R = –1) on aluminium lap joints, making it well suited for vibration-intensive assemblies.

Cure Cycle	130°C / 30 min / 0.5 MPa
Tg (cured)	≈95°C
Film Thickness	0.20–0.25 mm
T-Peel Strength	≥4 N/mm
Lap Shear Strength (Al–Al)	≥18 MPa

Thermosetting Acrylic Film Adhesive TAF-130

Specifications

FAQ

Interested in Thermosetting Acrylic Film Adhesive TAF-130?